Доступ предоставлен для: Guest
Портал Begell Электронная Бибилиотека e-Книги Журналы Справочники и Сборники статей Коллекции
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes
ESCI SJR: 0.176 SNIP: 0.48 CiteScore™: 1.3

ISSN Печать: 1093-3611
ISSN Онлайн: 1940-4360

Выпуски:
Том 24, 2020 Том 23, 2019 Том 22, 2018 Том 21, 2017 Том 20, 2016 Том 19, 2015 Том 18, 2014 Том 17, 2013 Том 16, 2012 Том 15, 2011 Том 14, 2010 Том 13, 2009 Том 12, 2008 Том 11, 2007 Том 10, 2006 Том 9, 2005 Том 8, 2004 Том 7, 2003 Том 6, 2002 Том 5, 2001 Том 4, 2000 Том 3, 1999 Том 2, 1998 Том 1, 1997

High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes

DOI: 10.1615/HighTempMatProc.2018026000
pages 345-352

FILM–SUBSTRATE SURFACE ALLOY FORMED BY AN INTENSE PULSED ELECTRON BEAM

Yurii F. Ivanov
National Research Tomsk Polytechnic University, 30 Lenin Ave., Tomsk, 634050, Russia; Institute of High Current Electronics, Siberian Branch of the Russian Academy of Sciences, 2/3 Akademichesky Ave., Tomsk, 634055, Russia
Nikolay N. Koval
Institute of High Current Electronics, Siberian Branch of the Russian Academy of Sciences, 2/3 Akademichesky Ave., Tomsk, 634055, Russia; National Research Tomsk State University, 36 Lenin Ave., Tomsk, 634050, Russia
Olga V. Krysina
Institute of High Current Electronics, Siberian Branch of the Russian Academy of Sciences, 2/3 Akademichesky Ave., Tomsk, 634055, Russia; Tomsk State University, Tomsk, Russia
P. V. Moskvin
Institute of High Current Electronics, SB RAS, 2/3 Akademichesky Ave., Tomsk, 634055, Russia
E. A. Petrikova
Institute of High Current Electronics, Siberian Branch of the Russian Academy of Sciences, 2/3 Akademichesky Ave., Tomsk, 634055, Russia
O. S. Tolkachev
Institute of High Current Electronics, Siberian Branch of the Russian Academy of Sciences, 2/3 Akademichesky Ave., Tomsk, 634055, Russia

Краткое описание

Commercially pure A7 aluminum was surface alloyed with commercially pure VT1-0 titanium on COMPLEX equipment under unified vacuum conditions through vacuum arc evaporation and deposition of a thin Ti film and irradiation of the film–substrate system with a submillisecond intense pulsed electron beam. The number of deposition–irradiation cycles was varied from 1 to 20. The film thickness in each cycle was 0.5 μm. After multicycle surface alloying, a multiphase surface layer was formed containing AlTi, Al2Ti, Al3Ti, TiAl3, and Al5Ti2 in addition to solid solutions based on Al and α-Ti. Increasing the number of deposition–irradiation cycles from 1 to 20 increased the relative content of intermetallic compounds in the surface layer. After 20 cycles, the modified material revealed an intermetallic surface layer consisting of a mixture of AlTi (53.3 wt.%), Al3Ti (36.6 wt.%), and Al5Ti2 (9.4 wt.%) with a submicro- and nanosized multilayer structure in the material bulk. The microhardness and the wear resistance of the modified material increased with the increasing number of cycles, and after 20 cycles, their values were respectively ≈ 8.5 and ≈ 45 times higher than those in A7 aluminum.


Articles with similar content:

SYNTHESIS OF SURFACE LAYERS HARDENED BY METAL TRIALUMINIDE COMPOUND IN Al−Si ALLOY UNDER COMPRESSION PLASMA FLOWS IMPACT
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.18, 2014, issue 1-2
Valiantsin M. Astashynski, Nikolai N. Cherenda, N. V. Bibik, A. M. Kuzmitski, Vladimir V. Uglov
AUSTENITIC STEEL SURFACE ALLOYED WITH ZIRCONIUM USING COMPRESSION PLASMA FLOW
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.16, 2012, issue 4
Valiantsin M. Astashynski, Nikolai N. Cherenda, E. A. Kostyukevich, A. M. Kuzmitski, A. H. Sari, Vladimir V. Uglov, Yu. A. Petukhou
ALUMINIDE COATINGS ON METALS BY A FLUIDIZED BED CVD PROCESS
Progress in Plasma Processing of Materials, 1997, Vol.1, 1997, issue
G. N. Angelopoulos, N. Voudouris
ELECTROEXPLOSIVE DOPING OF TITANIUM ALLOY BY BORON CARBIDE AND SUBSEQUENT ELECTRON BEAM PROCESSING
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.18, 2014, issue 4
V. E. Gromov, Yurii F. Ivanov, E. A. Budovskikh, T. A. Kobzareva, L. P. Bashchenko
MODIFICATION OF Al−20%Si HYPEREUTECTIC ALLOY STRUCTURE BY COMPRESSION PLASMA FLOW TREATMENT
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.17, 2013, issue 2-3
Valiantsin M. Astashynski, Nikolai N. Cherenda, S. V. Gusakova, A. M. Kuzmicki, A. P. Laskovnev, Vladimir V. Uglov