LOW-POWER LASER IGNITION OF ALUMINUM/METAL OXIDE NANOTHERMITES

Catalin Florin Petre
Defence Research and Development Canada – Valcartier, Québec, QC, G3J 1X5, Canada
Daniel Chamberland
Defence Research and Development Canada – Valcartier, Québec, QC, G3J 1X5, Canada
Tommy Ringuette
Numerica Technologies Inc., Québec (QC), G3J 1X5, Canada
Sophie Ringuette
Defence R&D Canada-Valcartier, Quebec City, Quebec G3J1X5, Canada
Suzanne Paradis
DRDC-Valcartier, Quebec, Canada
Robert Stowe
Defence Research and Development Canada, Quebec City, Quebec, Canada, G3J1X5

Краткое описание

In this study, three different types of nanothermites, i.e., Al/CuO, MoO3, and Al/Bi2O3, were produced using the widely spread wet (i.e., isopropanol based) method. In addition to the above method, the three nanothermites were also produced using a Resodyn LabRAM mixer. A paraffin-coated spherical Al nanopowder (100 nm) was used as the fuel source, while the oxidizers were nanometric powders of CuO (40 nm), MoO3 (100 nm), and Bi2O3 (200 nm). The effect of nanothermite composition on the sensitivity for the tests of electrostatic discharge (ESD), impact, and friction was investigated. Scanning electron microscopy (SEM) was used to analyze the morphology and homogeneity of the nanothermites. Next, the nanothermites were thermally analyzed in terms of energy release, ignition temperature, and flame temperature using a thermogravimetric analysis differential and scanning calorimetry (TGA/DSC) technique. A low-power diode laser was used to evaluate the ability of different laser wavelengths (661, 532, and 445 nm) to produce the ignition energy needed for a specific thermite reaction. Low ignition delays (less than 15 ms) were obtained at approximately 300 mW laser power output for both Al/MoO3 and Al/Bi2O3 thermites. Finally, a forward-looking infrared camera was used to estimate the ignition and burning temperatures of the Al/MoO3 nanothermite.


Articles with similar content:

EVALUATION OF NANO-Fe3O4 IN COMPOSITE PROPELLANT FORMULATIONS
International Journal of Energetic Materials and Chemical Propulsion, Vol.12, 2013, issue 6
D. R. Kshirsagar, P. P. Singh, B. Bhattacharya, Mehilal, Sudhir
THERMITE-BASED COMBUSTION SYNTHESIS OF NIOBIUM SILICIDES/Al2O3 COMPOSITES
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.16, 2012, issue 1
Yu-Shan Huang, Chun-Liang Yeh
FABRICATION AND CHARACTERIZATION OF AN AL/CR2O3/ETN ENERGETIC NANOCOMPOSITE VIA A SOL-GEL METHODOLOGY
International Journal of Energetic Materials and Chemical Propulsion, Vol.16, 2017, issue 4
Dan Song, Zhaoyang Song, Xiaolan Song, Yi Wang
PREPARATION AND CHARACTERIZATION OF SUBMICRON 3,3’-DIAMINO-4,4’-AZOXYFURAZAN
International Journal of Energetic Materials and Chemical Propulsion, Vol.15, 2016, issue 6
Xiao-Heng Geng, Yan Liu, Jin Luo, Jing-Yu Wang, Chongwei An
PREPARATION AND CHARACTERIZATION OF GRANULAR HYBRID REACTIVE MATERIALS
International Journal of Energetic Materials and Chemical Propulsion, Vol.9, 2010, issue 3
Yasmine Aly, Alexandre Ermoline, Mikhaylo A. Trunov, Mirko Schoenitz, Edward L. Dreizin