DOI: 10.1615/HighTempMatProc.v2.i3.50
pages 359-367

X-RAY DETERMINATION OF RESIDUAL STRESSES AND PHASE QUANTIFICATION IN Zr02 OXIDE LAYERS FORMED ON ZIRCALOY-4

J.L Bechade
CEREM/DECM/SRMA CEA-SACLAY - 91191 Gif sur Yvette Cedex - France
M. Gailhanou
Lab. de Metallurgie Physique - Universite de Poitiers - 86960 Futuroscope - France (°) LURE - Universite Paris-Sud - 91405 Orsay Cedex - France
P. Goudeau
CEREM/DECM/SRMA CEA-SACLAY - 91191 Gif sur Yvette Cedex - France
P. Yvon
CEREM/DECM/SRMA CEA-SACLAY - 91191 Gif sur Yvette Cedex - France

RESUMO

The residual stress state and the microstructure of Zr02 oxide layers formed on Zircaloy-4 plates in steam at 400°C were studied using x-ray diffraction techniques.
One of the most important features of the corrosion mechanism of Zircaloy is the development of compressive stresses within the oxide which strongly affect the microstructure of the growing oxide and the diffusion of oxidizing species. These compressive stresses can also favor the formation of tetragonal zirconia over monoclinic zirconia. Therefore, the accurate determination of the stress state and the composition of the oxide is essential for the understanding of the corrosion mechanism and the modelling of its kinetics.
The samples were prepared by oxidation of Zy-4 plates in an autoclave at 400°C in a vapor pressure of 10.3 MPa. Using conventional x-ray diffraction, it can be shown that the amount of tetragonal zirconia in the oxide layer decreases continuously with the oxidation time, however, with this type of radiation it is very difficult to obtain the phase distribution and the stress level profile in the oxide layer.
To obtain more accurate information, specific diffractometers on the French synchrotron radiation facility (LURE Orsay) were used to work at higher wavelengths. The following experimental results were obtained :
- High compressive stresses were found in the oxide layer and a strong effect of the oxide texture was observed.
- There seems to be a trend for the tetragonal zirconia to be preferentially located at the interface metal/oxide.


Articles with similar content:

STUDY ON BRAZING RESIDUAL STRESS OF STAINLESS STEEL WITH ALUMINA BY FINITE ELEMENT METHOD
ICHMT DIGITAL LIBRARY ONLINE, Vol.0, 2015, issue
Xionghui Li, Qiu-Wang Wang, Ting Ma, Min Zeng, Wenxiao Chu
PARAMETERS OF CHEMICAL VAPOR DEPOSITION ON A STRUCTURE AND THE PROPERTIES OF NANOSTRUCTURED TaC COATING ON A CARBON COMPOSITE MATERIAL
Nanoscience and Technology: An International Journal, Vol.5, 2014, issue 3
K. Chuprunov, A. Yudin, V. N. Anikin, Denis Leybo, S. A. Eremin, I. N. Burmistrov, D. V. Kuznetsov
FORMATION OF MICROSTRUCTURES AND OXIDES ON STRUCTURAL STEEL BY NANOSECOND LASER IRRADIATION
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.18, 2014, issue 3
C. Lupulescu, A. N. Chumakov, M. Mitric, B. Gakovic, Irina S. Nikonchuk, Suzana Petrovic
Measurement and Modeling of Emissivity of Roughened Titanium Surface at High Temperature
Proceedings of the 25th National and 3rd International ISHMT-ASTFE Heat and Mass Transfer Conference (IHMTC-2019), Vol.0, 2019, issue
C. V. Krishnamurthy, Sumeet Kumar, Krishnan Balasubramaniam
INFLUENCE OF MICROCRACKING ON PRESSURE-DEPENDENT ENERGETIC CRYSTAL COMBUSTION
International Journal of Energetic Materials and Chemical Propulsion, Vol.5, 2002, issue 1-6
W. L. Elban, Ronald W. Armstrong, C. F. Clark