High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes
ESCI SJR: 0.176 SNIP: 0.48 CiteScore™: 1.3

ISSN Imprimir: 1093-3611
ISSN On-line: 1940-4360

High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes

DOI: 10.1615/HighTempMatProc.v10.i3.80
pages 445-456

THERMAL STABILITY OF TiAlBN and TiN/TiCN COATINGS

A. Raveh
Division of Chemistry, NRC-Negev, P.O. Box 9001, Beer-Sheva 84190; and Ben-Gurion University, P.O. Box 653, Beer-Sheva 84105, Israel
I. Zukerman
Ben-Gurion University, P.O. Box 653, Beer-Sheva 84105, Israel
R. Z. Shneck
Ben-Gurion University, P.O. Box 653, Beer-Sheva 84105, Israel
R. Avni
Euro-Consultants (Israel), 10 Dov Friedman St. Ramat Gan, Israel
I. Fried
Euro-Consultants (Israel), 10 Dov Friedman St. Ramat Gan, Israel

RESUMO

Thermal stability of TiAlBN and TiN/TiCN hard coatings was studied by evaluating the stress-temperature curves and the wear resistance after annealing up to 1123 K. The microstructure, phase composition and hardness were studied prior and after annealing.
Prior to annealing, a correlation between the residual stress and hardness was observed. After annealing, the compressive stresses of the TiAlBN coatings decreased from 1.0 GPa to less than 0.2 GPa, while the hardness remained constant or increased from ~10 GPa to ~25 GPa. The hardness increase of the coatings after annealing is related to the self-hardening effect.
The effect of the plasma nitriding mode prior to the deposition of 3 μm thick TiCN or TiN/TiCN coatings on the wear resistance of the duplex-treated coating (nitriding and deposition) was studied. The stability of the wear resistance of the duplex treated-coating was also examined after one hour of annealing at 1123 K. It was found that the plasma-nitrided layer in the duplex treatment maintains the wear resistance stability of the annealed duplex-treated hard coatings.


Articles with similar content:

EFFECT OF THERMAL ANNEALING AND DEPOSITION CONDITIONS ON THE STRUCTURE AND MECHANICAL PROPERTIES OF A MULTILAYER NITRIDE COATING BASED ON Ta
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.20, 2016, issue 1
Pawel Drodziel, Valeriy Loboda, Olga Maksakova, Yaroslav O. Kravchenko
INFLUENCE OF HYDROGEN PLASMA TREATMENT ON THE STRUCTURE AND OPTICAL PROPERTIES OF TIN OXIDE THIN FILM PRODUCED BY MAGNETRON SPUTTERING
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.9, 2005, issue 2
I.V. Valitova, N. B. Beisenkhanov, Daniya M. Mukhamedshina, V. A. Botvin, K. A. Mit'
STUDY OF THE PHASES FORMED DURING THE GROWTH OF THICK COATINGS WITH COARSE GRAINED TIN
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.9, 2005, issue 2
G. Vourlias, E. Pavlidou, P. Patsalas, N. Pistofidis, E. K. Polychroniadis, G. Stergioudis
THE INFLUENCE OF COPPER ON MICROSTRUCTURE AND CATALYTIC PROPERTIES OF CEO2 THIN FILMS DEPOSITED BY PULSED LASER DEPOSITION
High Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes, Vol.7, 2003, issue 3
Ch. Leroux, J. R. Gavarri, R. Chmielowski, A. Kopia, S. Villain, J. Kusinski, S. Saiztek, M. Klimczak-Chmielowska
DURALIUM BEHAVIOR IN MULTISTAGE ARTIFICIAL AGING PROCESS
Nanoscience and Technology: An International Journal, Vol.8, 2017, issue 3
Poppy Puspitasari, Dewi Izza