FORMATION OF CONSOLIDATED NANOTHERMITE MATERIALS USING SUPPORT SUBSTRATES AND/OR BINDER MATERIALS

Jan A. Puszynski
Chemical and Biological Engineering Department, South Dakota School of Mines and Technology, Innovative Materials and Processes, LLC, Rapid City, South Dakota 57701
Chris J. Bulian
Chemical and Biological Engineering Department, South Dakota School of Mines and Technology, Rapid City, South Dakota 57701
Jacek J. Swiatkiewicz
Chemical and Biological Engineering Department, South Dakota School of Mines and Technology, Rapid City, South Dakota 57701
Deepak Kapoor
Armament Research, Development, and Engineering Center, Picatinny Arsenal, NJ 07806 USA

要約

Consolidated nanothermite felts with reduced sensitivity to electrostatic discharge for safer handling were produced without a significant reduction of the nanothermite reactivity. A polyester felt material with a thickness of 1.65 mm was easily infiltrated with a nanothermite slurry and the dried felt material prevented small particles from breaking off during handling. Combustion of 100 mg of the dried felt nanothermite in a closed-volume pressure cell generated higher pressure than those generated by nanothermite granules produced using a similar water-based processing method. The nanothermite felts also effectively absorbed nitrocellulose as a gasifying agent without a significant decrease in reaction rate. High-density reactive composites, based on tantalum metal fuel with a specific gravity of 16.6 and nanoscale Bi2O3 oxidizer, were formed with densities in excess of 5.0 g/cm3. THV 220A, a fluorocarbon polymer with oxidizing properties, was used as an effective binder in the composite. These materials were combined in acetone with tetrafluoroethylene, hexafluoropropylene, and vinylidene (THV), and after drying were pressed into pellets. Combustion of an 800-mg pellet lasted 5 s and was accompanied by the formation and ejection of hot particles from the surface of the pellet. Differential scanning calorimetry analysis determined that the ignition of the high-density composite occurs below 620 K, which is lower than common in nanothermite systems.


Articles with similar content:

IGNITER COMPOSITIONS FOR LOVA AND DOUBLE-BASE PROPELLANTS CONTAINING KDN
International Journal of Energetic Materials and Chemical Propulsion, Vol.18, 2019, issue 2
E. Roth, Stefan Kelzenberg, Sebastian Knapp, Volker Weiser, A. Koleczko
AMMONIUM DINITRAMIDE/GLYCIDYL AZIDE POLYMER (ADN/GAP) COMPOSITE PROPELLANTS WITH AND WITHOUT METALLIC FUELS
International Journal of Energetic Materials and Chemical Propulsion, Vol.16, 2017, issue 1
Volker Gettwert, Luigi T. DeLuca, Volker Weiser, Andrea Franzin, Manfred A. Bohn
SOL-GEL-SUPERCRITICAL SYNTHESIS AND PROPERTIES OF NITROCELLULOSE/GLYCIDYLAZIDE POLYMER/PENTAERYTHRITOL TETRANITRATE NANOCOMPOSITES
International Journal of Energetic Materials and Chemical Propulsion, Vol.19, 2020, issue 3
Mi Zhang, Hao Huang, Xiaolan Song, Yi Wang, Feifei Shang
OXIDATION, IGNITION AND COMBUSTION OF AL-HYDROCARBON COMPOSITE REACTIVE POWDERS
International Journal of Energetic Materials and Chemical Propulsion, Vol.11, 2012, issue 4
Shasha Zhang, Mirko Schoenitz, Edward L. Dreizin
MESOPOROUS Ni/NiO-SiO2 FOR EFFECTIVE HYDRODEOXYGENATION OF STEARIN INTO DIESEL RANGE HYDROCARBONS
Catalysis in Green Chemistry and Engineering, Vol.1, 2018, issue 2
Anil K. Sinha, Hari Singh